Cutback Bitumen
Cutback Bitumen is a type of dissolved bitumen. Solvent oils such as Gasoline or Kerosene are used to change bitumen into dissolved bitumen or liquid pitch. During consumption process, the solvent oil evaporates and the bitumen resides to obtain the desirable adhesion. Cut back grades are: Slow curing (70-250- 800-3000 ), Medium curing (0-1-2-3-4-5-30-70-250-800-3000) and Rapid curing (30-70 -250-800) |
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
MC-30
PROPERTY
MIN
MAX
TEST METHOD
Kinematics viscosity @60°C mm2/s
30
60
ASTM D2170
Distillate, volume percent of total
Distillate to 360°C
-
-
-
To 225°C
-
25
ASTM D402
To 260°C
40
70
ASTM D402
To 316°C
75
93
ASTM D402
Residue from distillation to 360°C, percent
volume by difference
50
-
ASTM D402
Tests on residue from distillation
-
-
-
Viscosity@60°C
30
120
ASTM D2170
Penetration@25°C
120
250
ASTM D5
Ductility@25°C
100
-
ASTM D113
Solubility in trichloroethylene, %
99
-
ASTM D2042
MC-70
PROPERTY
MIN
MAX
TEST METHOD
Kinematics viscosity @60°C mm2/s
70
140
ASTM D2170
Flash Point (Tag Open-Cup),°C
38
-
ASTM D3143
Distillate, volume percent of total
Distillate to 360°C
-
-
-
To 225°C
-
20
ASTM D402
To 260°C
20
60
ASTM D402
To 316°C
65
90
ASTM D402
Residue from distillation to 360°C, percent
volume by difference
55
-
ASTM D402
Tests on residue from distillation
-
-
-
Viscosity@60°C
30
120
ASTM D2170
Penetration@25°C
120
250
ASTM D5
Ductility@25°C
100
-
ASTM D113
Solubility in trichloroethylene, %
99
-
ASTM D2042
Water, %
-
0.2
ASTM D95
MC-250
PROPERTY
MIN
MAX
TEST METHOD
Kinematics viscosity @60°C mm2/s
250
500
ASTM D2170
Flash Point (Tag Open-Cup),°C
66
-
ASTM D3143
Distillate, volume percent of total
Distillate to 360°C
-
-
-
To 225°C
-
10
ASTM D402
To 260°C
15
55
ASTM D402
To 316°C
60
87
ASTM D402
Residue from distillation to 360°C, percent
volume by difference
67
-
ASTM D402
Tests on residue from distillation
-
-
-
Viscosity@60°C
30
120
ASTM D2170
Penetration@25°C
120
250
ASTM D5
Ductility@25°C
100
-
ASTM D113
Solubility in trichloroethylene, %
99
-
ASTM D2042
Water, %
-
0.2
ASTM D95
MC-800
PROPERTY
MIN
MAX
TEST METHOD
Kinematics viscosity @60°C mm2/s
800
1600
ASTM D2170
Flash Point (Tag Open-Cup),°C
66
-
ASTM D3143
Distillate, volume percent of total
Distillate to 360°C
-
-
-
To 225°C
-
-
ASTM D402
To 260°C
-
35
ASTM D402
To 316°C
45
80
ASTM D402
Residue from distillation to 360°C, percent
volume by difference
75
-
ASTM D402
Tests on residue from distillation
-
-
-
Viscosity@60°C
30
120
ASTM D2170
Penetration@25°C
120
250
ASTM D5
Ductility@25°C
100
-
ASTM D113
Solubility in trichloroethylene, %
99
-
ASTM D2042
Water, %
-
0.2
ASTM D95
MC-3000
PROPERTY
MIN
MAX
TEST METHOD
Kinematics viscosity @60°C mm2/s
3000
6000
ASTM D2170
Flash Point (Tag Open-Cup),°C
66
-
ASTM D3143
Distillate, volume percent of total
Distillate to 360°C
-
-
-
To 225°C
-
-
ASTM D402
To 260°C
-
15
ASTM D402
To 316°C
15
75
ASTM D402
Residue from distillation to 360°C, percent
volume by difference
80
-
ASTM D402
Tests on residue from distillation
-
-
-
Viscosity@60°C
30
120
ASTM D2170
Penetration@25°C
120
250
ASTM D5
Ductility@25°C
100
-
ASTM D113
Solubility in trichloroethylene, %
99
-
ASTM D2042
Water, %
-
0.2
ASTM D95
|
|